牌号简介 About
依凡坦33-45是由乙烯和醋酸乙烯经高压自由基聚合而成的无规共聚物。乙烯基醋酸盐含量高的Evatane 33-45具有柔软性、柔韧性和极性。Evatane 33-45与大多数增粘树脂和蜡兼容。它是一种高效易操作的热熔胶配方产品。Evatane 33-45与大多数填料具有高粘合强度,可用于生产HFFR化合物。也可用作原油添加剂(降凝剂)或沥青改性剂。它是一种理想的中压电缆用半导电化合物的基础聚合物。 EVATANE® 33-45 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. The high Vinyl Acetate content of EVATANE® 33-45 brings softness, flexibility and polarity. EVATANE® 33-45 is compatible with most tackifying resins and waxes. It is an efficient and easy handling product for hot melt adhesives formulations. EVATANE® 33-45 delivers high cohesive strength with most fillers and can be used to produce HFFR compounds. It can also be used as an additive for crude oil (pour point depressant), or bitumen modification. It is an ideal base polymer for semi-conductive compounds for medium voltage cables.

产品描述 Product Description
厂家:法国阿科玛 Arkema 类别:EVA EVA 用途:沥青改性;电线电缆应用;粘合剂; 性能特点: 柔软性好; 无规共聚物; 韧性好; Good flexibility,Random copolymer,Soft
技术参数 Technical Data
物理性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
密度 Density (73°F) 0.960 g/cm3 ISO 1183
熔体质量流动速率 熔体质量流动速率
190℃,2.16kg 190℃/2.16 kg 38 to 48 g/10min ASTM D1238
190℃,2.16kg 190℃/2.16 kg 38 to 48 g/10min ISO 1133
醋酸乙烯含量 Vinyl Acetate Content 32.0 to 34.0 wt% Internal Method
机械性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
邵氏硬度 邵氏硬度
邵氏 A 邵氏 A 63 ASTM D2240
邵氏 A 邵氏 A 63 ISO 868
拉伸强度 拉伸强度
断裂 断裂 9.00 MPa ASTM D638
断裂 断裂 9.00 MPa ISO 527-2
拉伸应变 拉伸应变
断裂 断裂 900 to 1100 % ASTM D638
断裂 断裂 900 to 1100 % ISO 527-2
热性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
维卡软化温度 Vicat Softening Temperature < 40.0 ℃ ASTM D1525 2
维卡软化温度 Vicat Softening Temperature < 40.0 ℃ ISO 306/A
熔融温度 Melting Temperature 62.0 ℃ ISO 11357-3
Ring and Ball Softening Point Ring and Ball Softening Point 3 3 107 ℃ ASTM E28