依凡坦28-40是由乙烯和醋酸乙烯经高压自由基聚合而成的无规共聚物。醋酸乙烯酯含量高的Evatane 28-40具有柔软性、柔韧性和极性。Evatane 28-40与大多数增粘树脂和蜡兼容。结合高流动性,它是一个高效和容易处理的产品热熔胶配方。Evatane 28-40与大多数填料具有高粘合强度,可用于生产HFFR化合物或母料。 EVATANE® 28-40 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. The high Vinyl Acetate content of EVATANE® 28-40 brings softness, flexibility and polarity. EVATANE® 28-40 is compatible with most tackifying resins and waxes. Combined with a high fluidity, it is an efficient and easy handling product for hot melt adhesives formulations. EVATANE® 28-40 delivers high cohesive strength with most fillers and can be used to produce HFFR compounds or masterbatches.

产品描述 Product Description
厂家:法国阿科玛 Arkema 类别:EVA EVA 用途:母料;粘合剂; 性能特点: 柔软性好; 无规共聚物; 流动性高; 韧性好; Good flexibility,High liquidity,Random copolymer,Soft
技术参数 Technical Data
物理性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
密度 Density (73°F) 0.950 g/cm3 ISO 1183
熔体质量流动速率 熔体质量流动速率
190℃,2.16kg 190℃/2.16 kg 35 to 45 g/10min ISO 1133
190℃,2.16kg 190℃/2.16 kg 35 to 45 g/10min ASTM D1238
醋酸乙烯含量 Vinyl Acetate Content 27.0 to 29.0 wt% Internal Method
机械性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
邵氏硬度 邵氏硬度
邵氏 A 邵氏 A 73 ISO 868
邵氏 A 邵氏 A 73 ASTM D2240
拉伸强度 拉伸强度
断裂 断裂 10.0 MPa ASTM D638
断裂 断裂 10.0 MPa ISO 527-2
拉伸应变 拉伸应变
断裂 断裂 800 to 1000 % ISO 527-2
断裂 断裂 800 to 1000 % ASTM D638
热性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
维卡软化温度 Vicat Softening Temperature < 40.0 ℃ ASTM D1525 2
维卡软化温度 Vicat Softening Temperature < 40.0 ℃ ISO 306/A
熔融温度 Melting Temperature 70.0 ℃ ISO 11357-3
Ring and Ball Softening Point Ring and Ball Softening Point 3 3 106 ℃ ASTM E28
备注
1 一般属性:这些不能被视为规格。
2 压 力1 (10N)
3 NF EN 1238