牌号简介 About
依凡坦18-150是由乙烯和醋酸乙烯经高压自由基聚合工艺制得的无规共聚物。醋酸乙烯酯含量高的18-500乙烯酯具有柔软性、柔韧性和极性。Evatane 18-500与大多数增粘树脂和蜡兼容。结合高流动性,它是一个高效和容易处理的产品热熔胶配方。也可用作沥青改性的添加剂。 EVATANE® 18-150 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. The high Vinyl Acetate content of EVATANE® 18-500 brings softness, flexibility and polarity. EVATANE® 18-500 is compatible with most tackifying resins and waxes. Combined with a high fluidity, it is an efficient and easy handling product for hot melt adhesives formulations. It can also be used as an additive for bitumen modification.

产品描述 Product Description
厂家:法国阿科玛 Arkema 类别:EVA EVA 用途:沥青改性;粘合剂; 性能特点: 柔软性好; 无规共聚物; 韧性好; 易流动; Good flexibility,Good liquidity,Random copolymer,Soft
技术参数 Technical Data
物理性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
密度 Density (73°F) 0.940 g/cm3 ISO 1183
熔体质量流动速率 熔体质量流动速率
190℃,2.16kg 190℃/2.16 kg 450 to 550 g/10min ASTM D1238
190℃,2.16kg 190℃/2.16 kg 450 to 550 g/10min ISO 1133
醋酸乙烯含量 Vinyl Acetate Content 17.0 to 19.0 wt%
机械性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
邵氏硬度 邵氏硬度
邵氏 A 邵氏 A 90 ASTM D2240
邵氏 A 邵氏 A 90 ISO 868
拉伸强度 拉伸强度
断裂 断裂 6.00 MPa ISO 527-2
断裂 断裂 6.00 MPa ASTM D638
拉伸应变 拉伸应变
断裂 断裂 600 to 900 % ASTM D638
断裂 断裂 600 to 900 % ISO 527-2
热性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
维卡软化温度 Vicat Softening Temperature 43.0 ℃ ASTM D1525 2
维卡软化温度 Vicat Softening Temperature 43.0 ℃ ISO 306/A
熔融温度 Melting Temperature 86.0 ℃ ISO 11357-3
Ring and Ball Softening Point Ring and Ball Softening Point 3 3 94 ℃ ASTM E28