牌号简介 About
OREVAC 18302N是一种经顺丁烯二酸酐改性的低密度聚乙烯,以颗粒形式提供。它可以在大多数设计用于加工传统聚烯烃的挤压设备上进行加工。应用:OREVAC 18302N的设计目的是在聚乙烯或大多数乙烯共聚物与多种不同材料(其中聚酰胺和EVOH)之间形成可靠的结合强度。OREVAC 18302N也推荐用于使用高负荷矿物填料的无卤阻燃电缆化合物中,这些填料需要优异的机械性能-断裂时的高拉伸强度、良好的延伸率和良好的耐化学性。 OREVAC® 18302N is a maleic anhydride modified low-density polyethylene available in pellet form. It can be processed on most extrusion equipments designed to process conventional polyolefin. Applications: OREVAC® 18302N has been designed to develop a reliable bonding strength between polyethylene or most ethylene copolymers and many kinds of different materials among which polyamides and EVOH. OREVAC® 18302N is also recommended in non-halogen flame retardant cable compounds using high loadings of mineral fillers which require outstanding mechanical properties - high tensile strength at break and good elongation and good chemical resistance.

产品描述 Product Description
厂家:法国阿科玛 Arkema 类别:LLDPE Linear low density polyethylene 用途:管道系统; 加工条件:共挤出成型 性能特点: 拉伸性能好; 无卤; 机械强度好; 耐化学性; 粘结性好; 阻燃; Good Rigidity,Halogen free,Flame Characteristics,Good bond,Good Tensile Strength,Solvent resistance
技术参数 Technical Data
物理性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
密度 Density 0.912 g/cm3 ASTM D1505
密度 Density 0.912 g/cm3 ISO 1183
熔体质量流动速率 熔体质量流动速率
190℃,2.16kg 190℃/2.16 kg 1.5 g/10min ASTM D1238
190℃,2.16kg 190℃/2.16 kg 1.5 g/10min ISO 1133
机械性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
拉伸强度 拉伸强度
断裂,模压成型 断裂,模压成型 20.0 MPa ASTM D638
断裂,模压成型 断裂,模压成型 20.0 MPa ISO 527-2
屈服,模压成型 屈服,模压成型 7.00 MPa ISO 527-2
屈服,模压成型 屈服,模压成型 7.00 MPa ASTM D638
拉伸应变 拉伸应变
断裂,模压成型 断裂,模压成型 790 % ISO 527-2
断裂,模压成型 断裂,模压成型 790 % ASTM D638
热性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
维卡软化温度 Vicat Softening Temperature 2 2 84.0 ℃ ASTM D1525 3
维卡软化温度 Vicat Softening Temperature 2 2 84.0 ℃ ISO 306/A
熔融温度 Melting Temperature 123 ℃ ISO 11357
备注
1 一般属性:这些不能被视为规格。
2 On compression molded samples
3 压 力1 (10N)